The durability of Portland cement mortars is often affected by environmental factors, which can cause physicochemical and mechanical degradation processes. In this study, the performance of three products, calcium acetoacetate and calcium tetrahydrofurfuryloxide dissolved in two different solvents developed and tested as stone consolidants, was evaluated in terms of crack filling or sealing and consolidation. Realistic cracks were induced in quasibrittle cement mortar prisms using a custom-designed test rig. The effectiveness and the performance of the considered treatments, investigated on specimens, were evaluated by optical and scanning electron microscopy, colourimetry, water absorption rate, ultrasonic pulse velocity, and surface hardness measurements. Results revealed that, in the examined conditions, the products were more suitable as surface consolidants than as crack fillers.
Innovative Calcium Carbonate-Based Products to Repair Cracked Cement Mortars
Garbin, Enrico;Panizza, Matteo;Artioli, Gilberto;
2022
Abstract
The durability of Portland cement mortars is often affected by environmental factors, which can cause physicochemical and mechanical degradation processes. In this study, the performance of three products, calcium acetoacetate and calcium tetrahydrofurfuryloxide dissolved in two different solvents developed and tested as stone consolidants, was evaluated in terms of crack filling or sealing and consolidation. Realistic cracks were induced in quasibrittle cement mortar prisms using a custom-designed test rig. The effectiveness and the performance of the considered treatments, investigated on specimens, were evaluated by optical and scanning electron microscopy, colourimetry, water absorption rate, ultrasonic pulse velocity, and surface hardness measurements. Results revealed that, in the examined conditions, the products were more suitable as surface consolidants than as crack fillers.File | Dimensione | Formato | |
---|---|---|---|
materials-15-04044.pdf
accesso aperto
Tipologia:
Published (publisher's version)
Licenza:
Creative commons
Dimensione
2.75 MB
Formato
Adobe PDF
|
2.75 MB | Adobe PDF | Visualizza/Apri |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.