A Calcium silicate hydrate (CSH) powder containing above 60 wt% xonotlite (remaining being tobermorite, scawtite and calcite) were produced from lime and ordinary recycled soda-lime glass via simple hydrothermal synthesis route. The thermogravimetric analysis demonstrated only ~20%weight loss up to 800 °C (at about the transformation temperature of CSHs to wollastonite), reaching a plateau in the 800-1200 °C temperature range. The synthesized CSH powder was employed for the fabrication of both green and heat-treated scaffolds by additive manufacturing (AM), possessing a high porosity (>80 vol%) and limited strength (~0.9 MPa).

Synthesis and additive manufacturing of calcium silicate hydrate scaffolds

Botti R.;Colombo P.;Vakifahmetoglu C.
2021

Abstract

A Calcium silicate hydrate (CSH) powder containing above 60 wt% xonotlite (remaining being tobermorite, scawtite and calcite) were produced from lime and ordinary recycled soda-lime glass via simple hydrothermal synthesis route. The thermogravimetric analysis demonstrated only ~20%weight loss up to 800 °C (at about the transformation temperature of CSHs to wollastonite), reaching a plateau in the 800-1200 °C temperature range. The synthesized CSH powder was employed for the fabrication of both green and heat-treated scaffolds by additive manufacturing (AM), possessing a high porosity (>80 vol%) and limited strength (~0.9 MPa).
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11577/3400914
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 17
  • ???jsp.display-item.citation.isi??? 16
  • OpenAlex ND
social impact