The structure and thermal evolution of Fe nanoparticles deposited on a wetting TiOx ultrathin film epitaxially grown on Pt(111) has been characterized by various surface science techniques. Combining the results obtained it is shown that, at room temperature, metallic Fe nucleates randomly and oxidizes at the interface. A thermal treatment causes Fe migration through the TiOx layer, forming a mixed oxide and a new hexagonal ultrathin film phase. Finally, the pristine TiOx phase motif is restored, due to the complete diffusion of Fe into the Pt substrate.
Interaction of iron with a wagon wheel-like ultrathin TiOxfilm grown on Pt(111)
ARTIGLIA, LUCA;RIZZI, GIAN-ANDREA
2015
Abstract
The structure and thermal evolution of Fe nanoparticles deposited on a wetting TiOx ultrathin film epitaxially grown on Pt(111) has been characterized by various surface science techniques. Combining the results obtained it is shown that, at room temperature, metallic Fe nucleates randomly and oxidizes at the interface. A thermal treatment causes Fe migration through the TiOx layer, forming a mixed oxide and a new hexagonal ultrathin film phase. Finally, the pristine TiOx phase motif is restored, due to the complete diffusion of Fe into the Pt substrate.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.