The influence of solution heat treatment time and temperature on the microstructure and mechanical properties and the mode of fracture of a high-pressure die-cast AlSi7MgMn alloy is reported. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes occurring during solution heat treatment. A solution heat treatment of 15 minutes at 475 degrees C, or even more at 525 degrees C, is sufficient to spheroidize the eutectic Si, as well as coarsen and increase the interparticle distance of the eutectic Si. Increasing the solutionizing temperature from 475 degrees C to 525 degrees C improves the mechanical properties.
Effect of solution heat treatments on the microstructure and mechanical properties of a die-cast AlSi7MgMn alloy
TIMELLI, GIULIO;
2008
Abstract
The influence of solution heat treatment time and temperature on the microstructure and mechanical properties and the mode of fracture of a high-pressure die-cast AlSi7MgMn alloy is reported. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes occurring during solution heat treatment. A solution heat treatment of 15 minutes at 475 degrees C, or even more at 525 degrees C, is sufficient to spheroidize the eutectic Si, as well as coarsen and increase the interparticle distance of the eutectic Si. Increasing the solutionizing temperature from 475 degrees C to 525 degrees C improves the mechanical properties.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.