The present work was devoted to the X-ray photoelectron spectroscopy (XPS) investigation of the principal core levels of a nanostructured Gd2O3 thin film. The sample was synthesized by metal organic chemical vapor deposition (MOCVD) from Gd((iPrN)2CNMe2)3 as precursor at 500 °C in an N2/O2 atmosphere. XPS results evidenced a marked Gd2O3 reactivity towards atmospheric CO2 and H2O, leading to a surface composition characterized by the co-presence of gadolinium carbonates/bicarbonates and hydroxides.
Gd2O3 nanostructured thin films analyzed by XPS
GASPAROTTO, ALBERTO;TONDELLO, EUGENIO;
2007
Abstract
The present work was devoted to the X-ray photoelectron spectroscopy (XPS) investigation of the principal core levels of a nanostructured Gd2O3 thin film. The sample was synthesized by metal organic chemical vapor deposition (MOCVD) from Gd((iPrN)2CNMe2)3 as precursor at 500 °C in an N2/O2 atmosphere. XPS results evidenced a marked Gd2O3 reactivity towards atmospheric CO2 and H2O, leading to a surface composition characterized by the co-presence of gadolinium carbonates/bicarbonates and hydroxides.File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.